Our Top-Coats
Technical Data Lubsil LS000
Product-No.: 9000 | IMDS-No.: 975042
Technical Datasheet
Lubricated Sealer for Zinc- and Zinc-alloys.
Features and Benefits
After application and drying, Lubsil LS000 forms an almost invisible, transparent seal with excellent corrosion protection and precise friction control - particularly suitable for passivated zinc and zinc alloys coated fasteners, applied dip-spin.
- Transparent coating
- Excellent adhesion to a wide variety of substrates
- No impairment of the material properties
- Economical consumption
- Improved corrosion protection
- Reliable fricition control (coefficient of friction)
Typical Applications
- Developed for coating and sealing zinc and zinc alloy substrates
- Compatible with all common passivations (blue, yellow, black, olive, etc.)
- Particularly efficient with Cr(VI)-free passivations and phosphates
- Meets and exceeds the corrosion protection requirements of the automotive industry
Application Remarks
- Lubsil LS000 is supplied ready for use and can be diluted with demineralized water if necessary (50-100% make up concentration).
- Parts to be coated must be free of grease.
- For optimum film formation, it is recommended to preheat the parts to 30-50 °C.
- Typical application process: Dip-spin process with coating centrifuges, alternatively drum coating or rack application
- After application, drying at 50-180 °C with hot air (e.g. chamber or continuous oven) is required.
- To avoid condensation, the parts should not be packaged until they have cooled down completely
Technical Data
| Property | Standard/ Parameter | Unit | Comments |
|---|---|---|---|
| Look | Visually | – | Transparent liquid |
| Density | DIN 51757 | g/cm³ | ~ 1,05 |
| Viscosity | DIN 53211 / 3 mm | s | 17 – 23 |
| Diluent | – | – | Water, de-ionized |
| pH | – | – | 10,0 - 11,5 |
| Packaging | – | – | 20 kg jerry can, 200 kg drum, 600/1000 kg IBC |
| Shelf life (sealed) | – | Months | 12 |
| Temp range in use | – | °C | -40 bis +200 |
| Coefficient of friction (typical) | µ | – | 0,09 - 0,13 |
| Coating Thickness | – | µm | 0,1 - 2,0 |
Additional notes
- The pH value of the solution should be checked regularly and always kept above 8.
- Avoid drag-in from previous process steps.
- Check the concentration of the bath regularly (exact instructions on request).
- Avoid strong agitation, as foaming may occur. Suitable defoamer: Lubsil AF-L
- Protect from frost!
The values stated correspond to the current state of our knowledge. These are average values which may vary within the scope of normal manufacturing fluctuations. We reserve the right to make further technical developments. Due to the different possible applications and conditions, the information provided is merely indicative. We recommend suitability tests of the product before use.